202 stainless steel plate, 202 stainless steel is one of the 200 series stainless steel. 200 series stainless steels are low-nickel and high-manganese stainless steels with a nickel content of less than 4% and a manganese content of about 8%. In order to transform the austenitic stainless steel, it must be heated above 1000 °C, so at 350 °C, the metallographic structure will not change, that is, the properties of the steel will not change drastically. It can only expand due to heating, but the amount is small and usually negligible. Therefore, 202 stainless steel belt has good high temperature resistance.
? Applications: architectural decoration, municipal engineering, highway guardrails, hotel facilities, shopping malls, glass handrails, public facilities and other places.
? Machinability: Cutting, forming and machining with appropriate equipment.
High nitrogen CrMnN austenitic stainless steel has the characteristics of non-magnetic, corrosion resistance, etc., and has a wide range of needs in the industry. In the future, there will be great development in the following aspects:
1. High nitrogen CrMnNiN steel with high strength, high corrosion resistance and good low temperature toughness can be used for aircraft, aerospace and ships to provide excellent performance of rods, wires, forgings, plates, sheets to make containers, pipes, valves, cables, etc.
2. Wear-resistant, corrosion-resistant, high-toughness and high-nitrogen CrMnN austenitic stainless steel can provide corrosion-resistant and wear-resistant mechanical equipment and materials for mining equipment for the mining industry.
3. Non-magnetic, high-strength, corrosion-resistant and high-nitrogen CrMnMoN austenitic stainless steel, which can provide non-magnetic drill collars for oil fields and non-magnetic retaining rings for power plant generators.
4. High resistance to pitting and crevice corrosion High nitrogen CrNiMnMoN austenitic stainless steel can provide materials for seawater heat exchangers, seawater desalination equipment, and smoke and sulfur removal devices in coastal factories.
Equivalent Material of 202 Stainless Steel plate
| China | Taiwan, China | Japan | Korea | United States | ISO | European standard | |||
| GB | ISC | CNS | JIS | KS | ASTM | UNS | EN | No. | |
| 112Cr18Mn9Ni5N | S35450 | 202 | SUS 202 | STS 202 | 202 | 202 | 202 | 202 | 1.4373 12Х17Г9АН4 |
| specification | Thickness:0.3-6.0mm 3.0mm*100mm | ||||||||
| Width:500-2000mm normal size1000 1219 1220 1240 1250 1500 2000mm Length:1000-6000mm normal size 2438 2440 3000 6000mm | |||||||||
| Mill | TISCO BAOSTEEL LISCO BAOXIN ZPSS JISCO | ||||||||
| Finish | 2b/No.1 | ||||||||
| Edge | Mill /raw or slit edge | ||||||||
| Weight | Thickness*Width*Length*7.93 per sheet | ||||||||
| Technique | cold rolled hot rolled | ||||||||
| Payment term | 30% T/T in advance,the balance before shipment | ||||||||
| Packing | 1.Export sea worthy package + water proof paper + wooden pallet 2.Max Loading 25mt for each 20GP container 3.Safe loading and fixing Professional Teams | ||||||||
| Delivery time | Within 7-10 working days after received 30%T/T of deposit or L/C original | ||||||||
| Trade terms | FOB SHANGHAI CFR&CIF your port | ||||||||
| Quality control | Mill Test Certificate is supplied with shipment | ||||||||
202 stainless steel composition content.
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 202 | Min. Max. |
≤0.15 | 7.5～10 | ≤1.00 | ≤0.05 | ≤0.03 | 17.0～19.0 | / | 4~6 | 0.05~0.25 |
| Tensile strength: ≥520MPa Yield strength: ≥275MPa Elongation: ≥40% Elastic Modulus: ≥400000 psi Rockwell hardness (HRB): ≤95 Density: .280 LBS/cubic inch (density 7.93g/cm3) |
||||||||||
202 Characteristic machining technology
1D — The surface has discontinuous granular shape, also known as fog surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2D – A slightly silvery white colour.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2B — Silver white with better gloss and flatness than a 2D surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + quenching and tempering rolling.
Ba – Excellent surface gloss, high reflectivity, like a mirror surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + surface polishing + quenching and tempering rolling.
No.3 — Good gloss, coarse grain surface.
Processing technology: polishing and tempering rolling for 2D or 2B with 100~120 abrasive materials (JIS R6002).
No.4 — Good gloss, fine lines on the surface.
Processing process: polishing and tempering rolling for 2D or 2B with 150~180 abrasive materials (JIS R6002).
HL — Silver grey with hair streaks.
Processing technology: 2D products or 2B products with appropriate granularity of abrasive materials for polishing the surface is a continuous abrasive grain.
MIRRO — Specular.
Processing technology: 2D products or 2B products with appropriate granularity of the grinding material grinding and polishing to the mirror effect.
Other special surfaces: color plating, water ripple, etching, anti-fingerprint, etc.
Stainless Steel 202 plate Price List
| Stainless Steel 202 plate Price List | 202 plate FOB Shanghai Per Unit (USD) | |||||||
| 2mm 202 stainless steel plate | $1500.00-$2000.00 | |||||||
| ss 202 mirror Stainless Steel plate/ Strip/ plate | $1800.00-$2300.00 | |||||||
| 202 Stainless Steel plate / Stainless Steel plate 202 | $1500.00-$2000.00 | |||||||
| Standard size 4×8 metal sus 202 grade stainless steel checkered plate prices | $1500.00-$2000.00 | |||||||